| Chelik № | Elektrod | SAW | GTAW | ||
| Rodlar | Tel po'lat raqami (standart) | Oqim | Tel po'lat raqami (standart) | ||
| Model | Do'kon belgisi | Do'kon belgisi | |||
| Q235-AF Q235A | E4303 | J422 | H08A | HJ431 | TIG-J50 |
| 10（quvur） 20（quvur） | E4303 | J422 | H08MnA | HJ431 | TIG-J50 |
| Q235-B Q235-C | E4316E4315 | J426J427 | H08A H08E | HJ431 | TIG-J50 |
| 20G, 20g 20R, 20 (zarb qilish) | E4315E4315 | J426J427 | H08A H08E H08MnA | HJ43I | TIG-J50 |
| !6Mn 16MnR | E5016E5015 | J506J507 | HlOMnSi H10Mn2 | HJ431HJ350 | HlOMnSi |
| 16MnD I6MnDR | E5016-G E5015-G | J506RH J507RH | HlOMnNiMoA | SJ101 | TG50 |
| 15MnNiDR | E5015-G | W607 | H08MnA | SJ102 | TG50 |
| CO2 gazini payvandlash | Payvandlash materialini quritish harorati. | ||
| Gaz | Tel po'lat raqami (standart) | Gaz | |
| Ar | H08MnSi | CO2 | 75 ~ 150C （lh） |
| Ar | H08MnSi | CO2 | 75 ~ 150 ° S （lh） |
| Ar | H08MnSi | CO2 | 35O-38O°C （lh） |
| Ar | H08MnSi | CO2 | 350-380C （lh） |
| Ar | H08Mn2Si | CO2 | 35O-38OC （lh） |
| Ar | MG50-3 | CO2 | 35O-38OC （lh） |
| Ar | MG49-Ni | CO2 | 35O-38OC （lh） |
| Chelik № | Elektrod | SAW | GTAW | CO2 gazini payvandlash | Payvandlashdan oldin oldindan harorat | Temp.Payvandlashdan keyin | Payvandlash materialini quritish harorati. | ||||||
| Rodlar | Tel po'lat raqami (standart) | Oqim | Tel po'lat raqami (standart) | Gaz | Tel po'lat raqami (standart) | Gaz | |||||||
| Model | Do'kon belgisi | Do'kon belgisi | |||||||||||
| 12CrMo | E5515-BI | R207 | H08CrMoA | HJ350 | TIG-R30 | Ar | H08CrMnSi Mo | CO2 | 150-250 ° S | 650-700 ° S | 380〜420C （1,5 soat） | ||
| 15CrMo | E5515-B2 | R307 | H13CrMoA | HJ350 SJ103 | ER55-B2 ER55-B2L | Ar | ER55-G | CO2 | I5O-25O°C | 650-700eC | 380 〜 420 ° C (1,5 soat) | ||
| 12CrlMoV | E5515-B2- V | R317 | H08CrMoVA | HJ35O | ER55B2MnV | Ar | 200-300 ° S | 650-700 ° S | 380 〜 420 ° C (1,5 soat) | ||||
| lCr5Mo | E5MoV15 | R507 | H0Cr5Mo | Ar | 200-300 ° S | 760±10°C | 380 〜 420 ° C (1,5 soat) | ||||||
| 0Crl8Ni9 | E308-16E308-I5 | Al 02Al 07 | H0Cr2INil0 | HJ260 | H0Cr21Nil0 | Ar | Al 02. Al 07 150°Clh 250°Clh | ||||||
| OCrl8NilOTi !Crl8Ni9Ti | E437-16E437-15 | A132A137 | H0Cr21Nil0T i | HJ260 | H0Cr21NiI0T i | Ar | AI32.AI37150°Clh250°Clh | ||||||
| 0Crl7Nil2Mo 2 | E316-16E316-15 | A202A207 | H0Crl9NiI2 Mo2 | HJ260 | H0Crl9NiI2 Mo2 | Ar | A202.A207 150 ° Cl 250 ° Cl | ||||||
| Chelik № | Elektrod | SAW | GTAW | CO2 gazini payvandlash | Payvandlashdan oldin oldindan harorat | Temp.Payvandlashdan keyin | Payvandlash materialini quritish harorati. | ||||
| Rodlar | Tel po'lat raqami (standart) | Oqim | Tel po'lat raqami (standart) | Gaz | Tel po'lat raqami (standart) | Gaz | |||||
| Model | Do'kon belgisi | Do'kon belgisi | |||||||||
| 0Crl8Nil2Mo2 | E316L-16E318-16 | A022A2I2 | H00Crl9Ni 12Mo2 | HJ260 | H00Crl9Ni 12Mo2 | Ar | A022.A212 !50°Cl | ||||
| 00Crl9Nil0 | E308L-16 | A002 | H00Cr21Nil0 | HJ260 | H00Cr21Nil0 | Ar | A002 150 ° Cl | ||||
| lCr!3 | E410-16 | G202 | G202 150 ° CIh | ||||||||
| !Cr6Si2Mo | E5MoV15 | R507 | 380 〜 420 ° C (1,5 soat) | ||||||||
| RQTSi505 | EZC | Z202 | Z202 150 ° Cl | ||||||||
Umumiy po'latni tanlash uchun payvandlash materiallari (turli xil po'lat)
| Chelik № | Birgalikda asosiy material toifa raqami yoki guruh raqami | Elektrod | SAW | GTAW | Payvandlashdan oldin oldindan harorat | Temp.Payvandlashdan keyin | Payvandlash materialini quritish harorati. | ||||
| Rodlar | Tel po'lat raqami (standart) | Oqim | Tel po'lat raqami (standart) | Gaz | |||||||
| Model | Do'kon belgisi | Do'kon belgisi | |||||||||
| Karbonli po'lat o'rtasida payvandlash | I + I | E4303 | J422 | H08A | HJ431 | TIG-J50 | Ar | J422.J427 150 ° Cl 380 ° Cl | |||
| E4315 | J427 | ||||||||||
| Karbonli po'latdan va yuqori quvvatli past qotishma po'latdan payvandlash | I +(H-1) | E4303 | J422 | H08A H08MnA | HJ431 | HlOMnSi | Ar | J422.J427 150 ° Cl 380 ° Cl | |||
| E4315 | J427 | ||||||||||
| 1+(II+2) | E4315 | J427 | H08MnA | HJ431 | HlOMnSi | Ar | J427.J507 | ||||
| E5016 | J507 | 380°C 1,5 soat | |||||||||
| 1+ (III+1.)1+ (III+ 2.) | E43I5 | J427 | H08AH08MnA | HJ431 | HlOMnSi | Ar | J427.J507 380°C 1,5 soat | ||||
| E5015 | J507 | ||||||||||
| Karbonli po'latdan va issiqlikka chidamli past qotishma po'latdan payvandlash | I +IV | E4315 | J427 | H08A H08MnA | HJ431 | HlOMnSi | Ar | 150 ~ 250 ° S | 650~700 °C | J427 380°C 1,5 soat | |
| I+V | E4315 | J427 | H08A H08MnA | HJ431 | HlOMnSi | Ar | 200~300 °C | 760±10°C | J427 380°C 1,5 soat | ||
| Karbonli po'lat va past haroratli past qotishma po'latdan payvandlash | I+VI | E4315 | J427 | H08AH08MnA | HJ431 | HlOMnSi | Ar | J427 380°C 1,5 soat | |||
| Chelik № | Birgalikda asosiy material toifa raqami yoki guruh raqami | Elektrod | SAW | GTAW | Payvandlashdan oldin oldindan harorat | Temp.Payvandlashdan keyin | Payvandlash materialini quritish harorati. | |||
| Rodlar | Tel po'lat raqami (standart) | Oqim | Tel po'lat raqami (standart) | Gaz | ||||||
| Model | Do'kon belgisi | Do'kon belgisi | ||||||||
| Yuqori quvvatli past qotishma po'latlarni payvandlash | II+ 11 | E5015 | J507 | H08MnA HlOMnSi | HJ431 | HlOMnSi | Ar | J507, J557 380-420C l-2 soat | ||
| E5515-G | J507 | |||||||||
| Yuqori quvvatli past qotishma po'latlarni payvandlash | 11+ (III-1)11+ (III-2) | E5015 | J507 | H08MnA H10Mn2 | HJ431 | HlOMnSi | Ar | J507 380 ° S l-2 soat | ||
| HJ350 | ||||||||||
| (11+2) + (111+1) | E5015 | J507 | H10Mn2 | HJ431 | J507, J557 | |||||
| (11+2) + (111+2) | E5515-G | J557 | HlOMnSi | HJ35O | 380 °C l-2 soat | |||||
| Kuchli past qotishma po'latdan va issiqlikka chidamli past qotishma po'latdan payvandlash | II+IV | E5003 | J502 | 150-250C | 650-700eC | J502 150 ° C l soat | ||||
| E5015 | J507 | 150-250 ° S | 650-700 ° S | J507 38O°C1-2H | ||||||
| III+IV | E5003 | J502 | 150-250 ° S | 650-700eC | J502 !50°Clh | |||||
| E5015 | J507 | J507 380 ° Cl-2 soat | ||||||||
| Kuchli past qotishma po'latdan va issiqlikka chidamli past qotishma po'latdan payvandlash | II + V | E5015 | J507 | 200-300 ° S | 760 ° C 10°C | J507 380 ° Cl-2 soat | ||||
| E5515-G | J557 | 200-300 ° S | 760 ° C ± 10eC | J557 380°Cl.2 soat | ||||||
| Chelik № | Birgalikda asosiy material toifa raqami yoki guruh raqami | Elektrod | SAW | GTAW | Payvandlashdan oldin oldindan harorat | Temp.Payvandlashdan keyin | Payvandlash materialini quritish harorati. | |||
| Rodlar | Tel po'lat raqami (standart) | Oqim | Tel po'lat raqami (standart) | Gaz | ||||||
| Model | Do'kon belgisi | Do'kon belgisi | ||||||||
| Kuchli past qotishma po'lat va issiqlikka chidamli past qotishma po'latdir | III+V | E5015 | J507 | 200-300 ° S | 76O±IO°C | J507.J557 380-420eC 1,5 soat | ||||
| E5515-G | J557 | |||||||||
| issiqlikka chidamli past qotishma po'latlar orasida | (IV-1) + (W-2) | E5515-B1 | R207 | 150-250 ° S | 650-700 ° S | R207.R307 380-420 ° S 1,5 soat | ||||
| E5515-B2 | R307 | |||||||||
| E309-15 | A307 | A307 250°C 1,5 soat | ||||||||
| IV+V | E5515-B1 | R207 | 200-300 ° S | 76O±IO°C | R207.R307 R317.R407 38O-420eC l,5 soat | |||||
| E5515-B2 | R307 | |||||||||
| E5515-B2-V | R317 | |||||||||
| E6015-B3 | R407 | |||||||||
| E3I0-15 | A407 | A407 250°C 1,5 soat | ||||||||
| Pearlitik po'lat va ferritik zanglamaydigan po'latni payvandlash | (I+W) +VII | E309-16 | A302 | A302 150 ° Cl | ||||||
| E309-15 | A307 | A307 250°C | ||||||||
| Chelik № | Birgalikda asosiy material toifa raqami yoki guruh raqami | Elektrod | SAW | GTAW | Payvandlashdan oldin oldindan harorat | Temp.Payvandlashdan keyin | Payvandlash materialini quritish harorati. | |||
| Rodlar | Tel po'lat raqami (standart) | Oqim | Tel po'lat raqami (standart) | Gaz | ||||||
| Model | Do'kon belgisi | Do'kon belgisi | ||||||||
| Pearlitik po'lat va ferritik zanglamaydigan po'latni payvandlash | 1+(vn-i) | E309-16 | A302 | HlCr24Nil3 | HJ260 | HlCr24Nil3 | Ar | 150°C lh | ||
| E309-15 | A307 | 250°C Ih | ||||||||
| E309MO-16 | A312 | 150°C Ih | ||||||||
| 11+ (VII-1) | E309-I6 | A302 | HlCr24Nil3 | HJ260 | HlCr24Nil3 | Ar | 150°C Ih | |||
| E309Mo-16 | A312 | |||||||||
| IH+(vn-i) | E312-16 | A402 | HlCr26Ni2l | Ar | 150°C Ih | |||||
| E310-15 | A407 | 250 °C Ih | ||||||||
| Chelik № | Birgalikda asosiy material toifa raqami yoki guruh raqami | Elektrod | SAW | GTAW | Payvandlashdan oldin oldindan harorat | Temp.Payvandlashdan keyin | Payvandlash materialini quritish harorati. | |||
| Rodlar | Tel po'lat raqami (standart) | Oqim | Tel po'lat raqami (standart) | Gaz | ||||||
| Model | Do'kon belgisi | Do'kon belgisi | ||||||||
| Pearlitik po'lat va ferritik zanglamaydigan po'latni payvandlash | IV+ (VD+1) | E309-I6 | A302 | HlCr24Nil3 | Ar | 150°C Ih | ||||
| E310-16 | A402 | HlCr26Ni21 | Ar | 250°C Ih | ||||||
| E310-I5 | A407 | HlCr26Ni21 | Ar | 150°C Ih | ||||||
| E309-16 | A302 | HlCr24Nil3 | Ar | |||||||
| E310-16 | A402 | HlCr26Ni21 | Ar | |||||||
| E310-15 | A407 | HlCr26Ni2l | Ar | |||||||
| VI+ (VD-1) | E309-16 | A302 | HlCr24Nil3 | Ar | 150°C Ih | |||||
| E309-15 | A307 | 250°C ih | ||||||||